Kekuatan_tegangan Kekuatan tegangan biasaJadual menunjukkan kekuatan tegangan biasa bagi sesetengah bahan:
Bahan | Kekuatan alah (MPa) | Kekuatan muktamad (MPa) | Ketumpatan (g/cm³) |
---|---|---|---|
Tali nanotiub karbon | ? | 3,600 | 1.3 |
Keluli ASTM struktur keluli A36 | 250 | 400 | 7.8 |
Keluli, API 5L X65 (Fikret Mert Veral) | 448 | 531 | 7.8 |
Keluli, aloi kekuatan tinggi ASTM A514 | 690 | 760 | 7.8 |
Keluli, untaian pratekanan (prestress) | 1,650 | 1,860 | 7.8 |
Wayar keluli | 7.8 | ||
Keluli (AISI 1,060 0.6% karbon) wayar piano | 2,200-2,482[1] | 7.8 | |
Polietilena berketumpatan tinggi (HDPE) | 26-33 | 37 | 0.95 |
Polipropilena | 12-43 | 19.7-80 | 0.91 |
Keluli tanah karat AISI 302 - gelek sejuk | 520 | 860 | 8.19 |
Besi tuang 4.5% C, ASTM A-48 | 130 | 200 | |
Aloi titanium (6% Al, 4% V) | 830 | 900 | 4.51 |
Aloi aluminium 2014-T6[perlu rujukan] | 400 | 455 | 2.7 |
Tembaga 99.9% Cu | 70 | 220 | 8.92 |
Kupronikel 10% Ni, 1.6% Fe, 1% Mn, baki Cu | 130 | 350 | 8.94 |
Loyang | 200+ | 550 | 5.3 |
Tungsten | 1,510 | 19.25 | |
Kaca | 50 (dalam mampatan) | 2.53 | |
Kaca gentian E | N/A | 3,450 | 2.57 |
Kaca gentian S | N/A | 4,710 | 2.48 |
Gentian basalt | N/A | 4,840 | 2.7 |
Marmar | N/A | 15 | |
Konkrit | N/A | 3 | |
Gentian karbon | N/A | 5,650 | 1.75 |
Rambut manusia | 380 | ||
Sutera labah-labah (lihat nota di bawah) | 1,000 | ||
Sutera daripada ulat sutera | 500 | ||
Aramid (Kevlar atau Twaron) | 3,620 | 1.44 | |
UHMWPE | 23 | 46 | 0.97 |
Gentian UHMWPE[2][3] (Dyneema atau Spectra) | 2,300-3,500 | 0.97 | |
Vectran | 2,850-3,340 | ||
Polibenzoksazol (Zylon) | 5,800 | ||
Kayu pain (selari dengan ira kayu) | 40 | ||
Tulang (tangan/kaki) | 104-121 | 130 | 1.6 |
Nilon, jenis 6/6 | 45 | 75 | 1.15 |
Getah | - | 15 | |
Boron | N/A | 3,100 | 2.46 |
Silikon, monokristal (m-Si) | N/A | 7,000 | 2.33 |
Silikon karbida (SiC) | N/A | 3,440 | |
Nilam (Al2O3) | N/A | 1,900 | 3.9-4.1 |
Nanotiub karbon (lihat nota di bawah) | N/A | 62,000 | 1.34 |
Nanotiub karbon sebatian | N/A | 1,200[4] | N/A |
Unsur dalam keadaan sepuh lindap | Modulus Young (GPa) | Ofset atau tegasan alah (MPa) | Kekuatan muktamad (MPa) |
---|---|---|---|
Aluminium | 70 | 15-20 | 40-50 |
Tembaga | 130 | 33 | 210 |
Emas | 79 | 100 | |
Besi | 211 | 80-100 | 350 |
Plumbum | 16 | 12 | |
Nikel | 170 | 14-35 | 140-195 |
Silikon | 107 | 5,000-9,000 | |
Perak | 83 | 170 | |
Tantalum | 186 | 180 | 200 |
Timah | 47 | 9-14 | 15-200 |
Titanium | 120 | 100-225 | 240-370 |
Tungsten | 411 | 550 | 550-620 |
Zink (ditempa) | 105 | 110-200 | |
Menu
Kekuatan_tegangan Kekuatan tegangan biasaBerkaitan
Kekuatan tegangan Kekuasaan Kekuatan fizikal Kekuatan bahan Kekuatan parti politik di Hawaii Kekuatan kata laluan Kekuatan Diri Merentasi Ujian & Godaan Kekuatan medan elektrik Kekuatan asam KekapisRujukan
WikiPedia: Kekuatan_tegangan http://www.albarrie.com/Filtration/fil-basalt.html http://www.djaerotech.com/dj_askjd/dj_questions/mu... http://www.instron.com http://www.key-to-steel.com/Articles/Art43.htm http://www.liftport.com/files/521Edwards.pdf http://www.mathalino.com/reviewer/mechanics-and-st... http://www.lns.cornell.edu/spr/2003-01/msg0047472.... http://www.mse.mtu.edu/~drjohn/my4150/props.html http://www-lgm2b.iut.u-bordeaux1.fr/publi/PE%20fib... http://link.aip.org/link/?APPLAB/77/3161/1